Manufacturer′s Exclusive Impact Modifier Agent - Chlorinated Polyethylene CPE135A

• Customization: Available
• CAS No.: 64754-90-1
• Formula: (C4h7cl)N
• Model NO.: 135A
• EINECS: No
• Certification: ISO9001
• Environmental Protection: Yes
• Color: White
• Kind: Plasticizer
• Appearance: Powder
• Company Proper: Manufacturer
• Sample: Yes
• Mode of Transport: Sea Transportation
• Product Color: White Powder
• Transport Package: 25kg/Bag
• Specification: 25kg/bag
• Trademark: AXA
• Origin: China
• HS Code: 39019090
• Production Capacity: 3000 Mt a Month

Product Description

Product Description

Bangtai  CPE-135A   is  a  thermoplastic  elastomer   material   made  of  chlorinated high-density polyethylene. CPE developed by our company has excellent elongation at break  and  excellent  toughness. This  product  is  a  saturated  thermoplastic  resin  with irregular structure. It has good extrusion fluidity when mixed with PVC. It is suitable for PVC hard products and molded products.

Product advantages
1 ,Excellent elongation at break and excellent powder fluidity;
2 ,Give PVC products good toughness;
3 ,Excellent hardness and tensile strength.

 

Product application

 

Technical Indicators

 

Parameter	Company	Test standard	CPE-135A
Product appearance	-	Visual inspection	White powder
Chlorine content	%	-	35±2
Apparent density	g/cm3	GB/T 1636-2008	0.50±0.10
Sieve  residue  (0.9mm sieve hole)	%	RK/PG-05-001	≤0.2
Volatile matter	%	RK/PG-05-003	≤0.4
Residual (750  C)	%	GB/T 9345-2008	≤5.0
Tensile strength	MPa	GB/T 528-2009	6-11
Elongation at break	%	GB/T 528-2009	600-1600
Hardness Shore A	-	GB/T 531-2008	≤65

packaging and storage

 

25kg  /  package.  Keep  the  product  clean  during  transportation  and  loading  and unloading  to  prevent  sun,  rain,  high  temperature  and  humidity  and  damage  to  the package.  It shall  be stored  in a cool,  dry warehouse without  direct sunlight and  at a temperature lower than 40ºC for two years. After two years, it can still be used after passing the performance inspection.