Chlorinated Polyethylene CPE135A PVC Processing Aid Impact Modifier

• Customization: Available
• Feature: Oxidative Degradable
• CAS No.: 64754-90-1
• Model NO.: 135A
• Formula: [CH2-Chcl-CH2-CH2]N
• Material: Polyvinyl Chloride/PVC
• Usage: General Plastics
• Color: White
• Company Proper: Manufacturer
• Mode of Transport: Sea Transportation
• Product Color: White Powder
• Sample: Yes
• Transport Package: Bag
• Specification: 25kg/bag
• Trademark: AXA
• Origin: China
• HS Code: 39019090
• Production Capacity: 50000 Tons/Year

Product Description

Product Introduction

AXA  CPE-135A   is  a  thermoplastic  elastomer   material   made  of  chlorinated high-density polyethylene. CPE developed by our company has excellent elongation at break  and  excellent  toughness. This  product  is  a  saturated  thermoplastic  resin  with irregular structure. It has good extrusion fluidity when mixed with PVC. It is suitable for PVC hard products and molded products.

CPE135A is the main PVC impact modifier with double performance of the plastic and rubber. This product has good weatherability, oil resistance, ozone resistance, flame resistance and good histocompatibility with varied plastics and rubber. It can effectively improve toughness and impact resistance and anti-aging of rigid PVC products, to increase the melting point of PVC.

 

Product advantages

1Excellent elongation at break and excellent powder fluidity;
2Give PVC products good toughness;
3Excellent hardness and tensile strength.

Product application

CPE-135A  is  widely  used  in  toughening  and  modification  of  PVC  hard products, such as PVC door and window profiles, PVC pipes, PVC gusset plates, wood plastics and other fields.

 

Technical Indicators

Parameter	Company	Test standard	CPE-135A
Product appearance	-	Visual inspection	White powder
Chlorine content	%	-	35±2
Apparent density	g/cm3	GB/T 1636-2008	0.50±0.10
Sieve  residue  (0.9mm sieve hole)	%	RK/PG-05-001	≤0.2
Volatile matter	%	RK/PG-05-003	≤0.4
Residual (750  C)	%	GB/T 9345-2008	≤5.0
Tensile strength	MPa	GB/T 528-2009	6-11
Elongation at break	%	GB/T 528-2009	600-1600
Hardness Shore A	-	GB/T 531-2008	≤65

packaging and storage

 

Our product is sealed in plastic bags and then externally packaged in polypropylene bags, each weighing 25±0.1kg. 

Storage and Transportation
Keep  the  product  clean  during  transportation  and  loading  and unloading  to  prevent  sun,  rain,  high  temperature  and  humidity  and  damage  to  the package.  It shall  be stored  in a cool,  dry warehouse without  direct sunlight and  at a temperature lower than 40ºC for two years. After two years, it can still be used after passing the performance inspection.