| parameter | unit | Testing Standard | CPE-135B |
| Appearance | - | visual inspection | White powder |
| Chlorine content | % | - | 35±2 |
| Apparent density | g/cm3 | GB/T1636-2008 | 0.50±0.10 |
| Sieve residue (0.9mm sieve hole) | % | RK/PG-05-001 | ≤0.2 |
| Volatile matter | % | RK/PG-05-003 | ≤0.4 |
| Residue (750°C) | % | GB/T 9345-2008 | ≤5.0 |
| Tensile Strength | MPa | GB/T 528-2009 | 6-11 |
| elongation at break | % | GB/T 528-2009 | 600-1600 |
| Hardness Shore A | - | GB/T 531-2008 | ≤65 |
| Mooney viscosity | ML(1+4)125ºC | - | 45-95 |
AXA CPE-135B is a thermoplastic elastomer material made of chlorinated high-density polyethylene. This strain is an irregular structure and thermoplastic elastomer, almost completely free of crystals, with excellent flame retardancy, electrical insulation, chemical resistance, oil resistance and water resistance. Good compatibility with PVC, CR, NBR, etc. It can be used as a flame retardant for ABS products, housings for electric wires and electrical appliances, and soft PVC foaming materials. It can also be used as a special synthetic rubber, as a modifier for general synthetic rubber and as a plasticizer for plastics such as PVC.
1. Excellent elongation at break
2. Excellent flame retardant performance
3. Excellent powder fluidity
4. Excellent electrical insulation performance
25Kg/bag, the product should be kept clean during transportation and loading and unloading, avoid sun, rain, high temperature and humidity, and avoid damage to the packaging. It should be stored in a cool, dry warehouse without direct sunlight and at a temperature below 40°C. The storage period is two years. It can still be used after passing the performance inspection after two years.