| Customization: | Available |
|---|---|
| CAS No.: | 64754-90-1 |
| Formula: | [CH2-Chcl-CH2-CH2]N |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
AXA CPE-135B is a thermoplastic elastomer material made of chlorinated high-density polyethylene. This strain is an irregular structure and thermoplastic elastomer, almost completely free of crystals, with excellent flame retardancy, electrical insulation, chemical resistance, oil resistance and water resistance. Good compatibility with PVC, CR, NBR, etc. It can be used as a flame retardant for ABS products, housings for electric wires and electrical appliances, and soft PVC foaming materials. It can also be used as a special synthetic rubber, as a modifier for general synthetic rubber and as a plasticizer for plastics such as PVC.
1 ,Excellent elongation at break and excellent powder fluidity;
2 ,Give PVC products good toughness;
3 ,Excellent hardness and tensile strength.
| parameter | unit | Testing Standard | CPE-135B |
| Appearance | - | visual inspection | White powder |
| Chlorine content | % | - | 35±2 |
| Apparent density | g/cm3 | GB/T1636-2008 | 0.50±0.10 |
| Sieve residue (0.9mm sieve hole) | % | RK/PG-05-001 | ≤0.2 |
| Volatile matter | % | RK/PG-05-003 | ≤0.4 |
| Residue (750°C) | % | GB/T 9345-2008 | ≤5.0 |
| Tensile Strength | MPa | GB/T 528-2009 | 6-11 |
| elongation at break | % | GB/T 528-2009 | 600-1600 |
| Hardness Shore A | - | GB/T 531-2008 | ≤65 |
| Mooney viscosity | ML(1+4)125ºC | - | 45-95 |
25kg / package. Keep the product clean during transportation and loading and unloading to prevent sun, rain, high temperature and humidity and damage to the package. It shall be stored in a cool, dry warehouse without direct sunlight and at a temperature lower than 40ºC for two years. After two years, it can still be used after passing the performance inspection.