AXA CPE-135B is a thermoplastic elastomer material made of chlorinated high-density polyethylene. This strain is an irregular structure and thermoplastic elastomer, almost completely free of crystals, with excellent flame retardancy, electrical insulation, chemical resistance, oil resistance and water resistance. Good compatibility with PVC, CR, NBR, etc. It can be used as a flame retardant for ABS products, housings for electric wires and electrical appliances, and soft PVC foaming materials. It can also be used as a special synthetic rubber, as a modifier for general synthetic rubber and as a plasticizer for plastics such as PVC.
| Parameter | Unit | Test Standard | CPE-135BA(CM Series Included) |
| Product Appearance | -- | Visual Inspection | White Power |
| Chlorine Content | % | -- | 35±2 |
| Apparent Density | G/Cm³ | GB/T1636-2008 | 0.50±0.10 |
| Sieve Residue(0.9mm Sieve Hole) | % | RK/PG-05-001 | ≤0.2 |
| Volatile Matter | % | RK/PG-05-003 | ≤0.4 |
| Residual(750ºC) | % | GB/T9345-2008 | ≤0.5 |
| Tensile Strength | MPa | GB/T528-2009 | 6-11 |
| Elongation At Break | % | GB/T528-2009 | >800 |
| Hardness Shote A | -- | GB/T531-2008 | ≤65 |
| Mooney Viscosity | ML(1+4)125ºC | -- | 40-95 |
CPE-135B is a thermoplastic elastomer material made of chlorinated high-density polyethylene. This strain is an irregular structure and thermoplastic elastomer, almost completely crystal free, with excellent flame retardancy, electrical insulation, chemical resistance, oil resistance, and water resistance. It has good compatibility with PVC, CR, NBR, etc. It can be used as a flame retardant for ABS products, wire and appliance casings, and soft PVC foam materials. It can also be used as a special synthetic rubber, as a modifier for ordinary synthetic rubber, and as a plasticizer for plastics such as PVC.
25Kg/bag, the product should be kept clean during transportation and loading and unloading, avoid sun, rain, high temperature and humidity, and avoid damage to the packaging. It should be stored in a cool, dry warehouse without direct sunlight and at a temperature below 40°C. The storage period is two years. It can still be used after passing the performance inspection after two years.