| Customization: | Available |
|---|---|
| CAS No.: | 64754-90-1 |
| Formula: | [CH2-Chcl-CH2-CH2]N |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Parameter | Unit | Test Standard | CPE-135BA(CM Series Included) |
| Product Appearance | -- | Visual Inspection | White Power |
| Chlorine Content | % | -- | 35±2 |
| Apparent Density | G/Cm³ | GB/T1636-2008 | 0.50±0.10 |
| Sieve Residue(0.9mm Sieve Hole) | % | RK/PG-05-001 | ≤0.2 |
| Volatile Matter | % | RK/PG-05-003 | ≤0.4 |
| Residual(750ºC) | % | GB/T9345-2008 | ≤0.5 |
| Tensile Strength | MPa | GB/T528-2009 | 6-11 |
| Elongation At Break | % | GB/T528-2009 | >800 |
| Hardness Shote A | -- | GB/T531-2008 | ≤65 |
| Mooney Viscosity | ML(1+4)125ºC | -- | 40-95 |
CPE-135B is a thermoplastic elastomer material made of chlorinated high-density polyethylene. This strain is an irregular structure and thermoplastic elastomer, almost completely crystal free, with excellent flame retardancy, electrical insulation, chemical resistance, oil resistance, and water resistance. It has good compatibility with PVC, CR, NBR, etc. It can be used as a flame retardant for ABS products, wire and appliance casings, and soft PVC foam materials. It can also be used as a special synthetic rubber, as a modifier for ordinary synthetic rubber, and as a plasticizer for plastics such as PVC.
1. 25kg polypropylene packaging bags, or customized packaging according to customer requirements.
2. During the transportation and loading and unloading of products, it should be kept clean to prevent sun and rain, high temperature and humidity, and avoid damage to the packaging. The products should be stored in a cool, dry, no direct sunlight, temperature below 40 °C warehouse, storage period of two years, the products can still be useful if the performance test qualified two years later.