CPE-135A is a thermoplastic elastomer material made of chlorinated high-density polyethylene. CPE developed by our company has excellent elongation at break and excellent toughness. This product is a saturated thermoplastic resin with irregular structure. It has good extrusion fluidity when mixed with PVC. It is suitable for PVC hard products and molded products.
1.Excellent elongation at break and excellent powder fluidity;
2.Give PVC products good toughness;
3.Excellent hardness and tensile strength.
| Parameter | Company | Test standard | CPE-135A |
| Product appearance | - | Visual inspection | White powder |
| Chlorine content | % | - | 35±2 |
| Apparent density | g/cm3 | GB/T 1636-2008 | 0.50±0.10 |
| Sieve residue (0.9mm sieve hole) | % | RK/PG-05-001 | ≤0.2 |
| Volatile matter | % | RK/PG-05-003 | ≤0.4 |
| Residual (750 C) | % | GB/T 9345-2008 | ≤5.0 |
| Tensile strength | MPa | GB/T 528-2009 | 6-11 |
| Elongation at break | % | GB/T 528-2009 | 600-1600 |
| Hardness Shore A | - | GB/T 531-2008 | ≤65 |
CPE-135A is widely used in toughening and modification of PVC hard products, such as PVC door and window profiles, PVC pipes, PVC gusset plates, wood plastics and other fields.
25kg / package. Keep the product clean during transportation and loading and unloading to prevent sun, rain, high temperature and humidity and damage to the package. It shall be stored in a cool, dry warehouse without direct sunlight and at a temperature lower than 40ºC for two years. After two years, it can still be used after passing the performance inspection.